FUNDICIÓN
|
FUNDICIÓN GRIS/LAMINAR
|
|
|
NORMAS PAISES |
EN 1561:1997 |
UK |
GERMANY |
FRANCIA |
ITALY |
USA |
JAPAN |
SIMBOLO |
NUMERO |
BS1452 |
DIN1691 |
NFA 32-101 |
UNI 5007 |
ASTMA48M-94 |
JIS G5501 |
EN GJL-100 |
ENJL 1010 |
100 |
GG-10 |
|
G10 |
|
FC100 |
EN GJL-150 |
ENJL 1020 |
150 |
GG-15 |
FGL 150 |
G15 |
150/175 |
FC150 |
EN GJL-200 |
ENJL 1030 |
200/220 |
GG-20 |
FGL 200 |
G20 |
200/225 |
FC200 |
EN GJL-250 |
ENJL 1040 |
250 |
GG-25 |
FGL 250 |
G25 |
250/275 |
FC250 |
EN GJL-300 |
ENJL 1050 |
300 |
GG-30 |
FGL 300 |
G30 |
300/325 |
FC300 |
|
|
|
|
|
|
|
|
|
|
|
FUNDICIÓN NODULAR/ESFEROIDAL
|
|
|
NORMAS PAISES |
EN 1561:1997 |
UK |
GERMANY |
FRANCIA |
ITALY |
USA |
JAPAN |
SIMBOLO |
NUMERO |
BS2789 |
DIN1693 |
NF A32-201 |
UNI 4544 |
ASTM A536 |
JIS G5502 |
EN GJS-350 22LT |
EN-JS1015 |
350/22 L40 |
GGG-35.3 |
350-22 L40 |
GS370-17 |
|
FCD 350-22 L |
EN GJS-350 22RT |
EN-JS1014 |
|
|
350-22 |
|
|
|
EN GJS-350 22 |
EN-JS1010 |
350/22 |
|
|
|
|
FCD 350-22 |
EN GJS-400 -18-LT |
EN-JS1025 |
400/18 L20 |
GGG-40.3 |
400-18 L20 |
|
|
FCD 400-18L |
EN GJS-400-18-RT |
EN-JS1024 |
|
|
|
|
|
|
EN GJS-400-18 |
EN-JS1020 |
400/18 |
|
400-18 |
|
60-40-18 |
FCD 400-18 |
EN GJS-400-15 |
EN-JS1030 |
400/12 |
GGG-40 |
400-15 |
GS400-12 |
65-45-12 |
FCD 400-15 |
EN GJS-450-10 |
EN-JS1040 |
450/10 |
|
450-10 |
|
70-50-05 |
FCD 450-10 |
EN GJS-500-7 |
EN-JS1050 |
500/7 |
GGG-50 |
500-7 |
GS500-7 |
80-55-06 |
FCD 500-7 |
EN GJS-600-3 |
EN-JS1060 |
600/3 |
GGG-60 |
600-3 |
GS600-3 |
100-70-03 |
FCD 600-3 |
EN GJS-700-2 |
EN-JS1070 |
700/2 |
GGG-70 |
700-2 |
GS700-2 |
|
FCD 700-2 |
EN GJS-800-2 |
EN-JS1080 |
800/2 |
GGG-80 |
800-2 |
GS800-2 |
120-90-02 |
FCD 800-2 |
EN GJS-900-2 |
EN-JS1090 |
900/2 |
|
900-2 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ACEROS
|
Symbol |
DIN |
UNS |
|
ACEROS CON CARBONO BAJO Y MEDIO BAJO
|
|
ACEROS CON CARBONO MEDIO ALTO Y ALTO
|
C-15 |
10.401 |
|
|
GS-38 |
20Mn5N |
BS3100 A4 |
|
GS-52 |
30Mn5N |
BS3100A5 |
S355JRC |
10.551 |
|
|
GS-45 |
20Mn5V |
1.0619 |
|
GS-60 |
30Mn5V |
|
A216 WCB |
10.619 |
J03002 |
|
WCA |
LCA |
A27 (60-30) |
|
C35E |
|
A-148 (90-60) |
GP240GH |
10.619 |
|
|
WCB |
LCB |
A27 (65-35) |
|
C45E |
|
|
F-114 |
11.140 |
|
|
WCC |
LCC |
GP240GH |
|
|
|
|
A352 LCB |
11.156 |
J03003 |
|
|
|
|
|
|
|
|
42CrMo4 |
13.563 |
|
|
|
|
|
|
|
|
|
G42CrMo4 |
13.563 |
|
|
ACEROS ALEADOS
|
|
ACEROS ALTA ALEACION E INOXIDABLES
|
A217 CA15 |
14.006 |
J91150 |
|
WC1 |
25CrMo4 |
22CrNiMo5.6 |
|
CF3 |
1.4309 |
304L |
AISI 410 |
14.006 |
S41000 |
|
WC6 |
34CrMo4 |
14CrMoV 6.9 |
|
CF3M |
1.4409 |
316L |
AISI 420 |
14.021 |
S42000 |
|
WC9 |
42CrMo4 |
|
|
CF8 |
1.4308 |
304 |
GX20Cr14 |
14.027 |
|
|
G17CrMo5-5 |
GS40MnSi5 |
|
|
CF8M |
1.4408 |
316 |
AISI 431 |
14.057 |
S43100 |
|
G17CrNiMo13.6 |
|
|
|
|
1.4462 |
A890 |
GX70Cr29 |
14.085 |
|
|
G18NiMoCr 3.6 |
|
|
|
|
1.4416 |
904L |
GX120Cr29 |
14.086 |
|
|
|
|
|
|
|
|
CA15 |
GX70CrMo29-2 |
14.136 |
|
|
|
|
|
|
|
|
CA40 |
A351 CF8 |
14.308 |
J92600 |
|
|
|
|
|
CA6NM |
1.4317 |
GX4CrNi13-4 |
A351 CF8A |
14.308 |
J92600 |
|
|
|
|
|
|
|
|
A351 CF8M |
14.408 |
J92900 |
|
|
|
|
|
|
|
|
GX5CrNiMo19-11-2 |
14.408 |
|
|
ACEROS AL CARBONO Y ALEADOS
|
AISI 317 |
14.449 |
S31700 |
|
DESCRIPCION |
EQUIVALENTES |
COMPOSICION QUIMICA |
PROPIEDADES |
A890 Gr3A |
14.460 |
J93371 |
|
|
%C %Mn %SI %P %S %Ni % Cr %Mo % V |
|
GX2CrNiMoN25-6-3 |
14.468 |
|
|
GS-45 |
ASTM A27 grade 65-35 |
0,20 0,80 0,35 0,025 0,025 |
R>45kg/mm2 |
A890 Gr4A |
14.470 |
J92205 |
|
GS-60 |
|
0,40 0,80 0,35 0,025 0,025 |
R>60kg/mm2 |
GX2CrNiMoCuN25-6-3-3 |
14.517 |
|
|
GS-C25 |
ASTM A216 WCA |
0,23 0,80 0,60 0,020 0,015 |
R>50kg/mm2 |
AISI 904 L |
14.539 |
N08904 |
|
GS-20Mn5 |
ASTM A216 WCC |
0,23 1,50 0,60 0,020 0,015 |
R>55kg/mm2 |
A747 ( CB7Cu-1) |
14.542 |
|
|
GS-25CrMo4 |
ASTM A752 grade41-30 |
0,25 0,80 0,60 0,020 0,015 1,00 0,25 |
R>90kg/mm2 |
GX40 CrNiSi27-4 |
14.823 |
|
|
GS-42CrMo4 |
|
0,45 1,00 0,50 0,020 0,015 1,00 0,25 |
R>85kg/mm2 |
GX40CrNiSi22-9 |
14.826 |
|
|
GS-15NiMoCr3.6 |
|
0,22 1,00 0,60 0,020 0,015 0,6 0,80 |
R>70kg/mm2 |
AISI 309 |
14.828 |
S30900 |
|
GS-24Mn6 |
SEW 520 |
0,40 1,80 0,60 0,020 0,020 |
R>65kg/mm2 |
A351 CH8 |
14.833 |
J93400 |
|
GS-30CrMo V6-4 |
SEW 515 |
0,30 0,80 0,60 0,020 0,015 1,50 0,4 0,10 |
R>85kg/mm2 |
AISI 309 S |
14.833 |
S30908 |
|
GS-22NiMoCr 5-6 |
SEW 520 |
0,20 1,00 0,60 0,015 0,015 1,0 0,8 0,6 |
R>100kg/mm2 |
AISI 310 |
14.841 |
S31000 |
|
|
|
|
|
A351 CK20 |
14.843 |
J94202 |
|
ACEROS Y FUNDICIONES RESISTENTES AL DESGASTE
|
GX23CrMoV12-1 |
14.931 |
|
|
DESCRIPCION |
EQUIVALENTES |
COMPOSICION QUIMICA |
PROPIEDADES |
F-127 |
16.743 |
|
|
|
|
%C %Mn %Ni % Cr %Mo % V % Si |
|
A 352 LC 2-1 |
16.783 |
J42215 |
|
GX280CrMoNi 20.2.1 |
ASTM A532 CL II E |
2,80 0,80 0,90 20,00 2,00 |
>60HRc |
GX6CrNi18-10 |
16.902 |
|
|
GX340CrMo27.2 |
|
3,40 0,80 28,00 2,00 |
>62HRc |
25CD4 |
17.218 |
|
|
GX300Cr 13 |
ASTM A532 CL II A |
3,00 0,60 13,00 |
>45HRc |
34CrMo4 |
17.220 |
|
|
GX200Cr 13 |
|
1,80 0,30 13,00 <2,00 |
>58HRc |
F-125 |
17.220 |
|
|
GX165CrMoV 12 |
|
1,65 0,30 13,00 1,00 |
>58HRc |
A217 WC6 |
17.357 |
J12072 |
|
GX300NiCr4.2 |
ASTM A532 CL I A,B,C |
3,00 0,60 4,00 2,00 |
>54HRc |
G17CrMo5-5 |
17.357 |
|
|
GX300CrNiSi 9.5.2 |
ASTM A532 CL I D |
3,00 0,60 6,00 8,00 |
>58HRc |
A217 C5 |
17.363 |
J42045 |
|
GX260/Cr27 |
ASTM A532 CL III A |
2,60 0,80 27,00 |
>55HRc |
A217 WC9 |
17.380 |
J21890 |
|
CrMo |
|
0,40 0,70 3,00 0,50 |
>48HRc |
Inconel 600 |
24.816 |
|
|
|
|
|
|
|
|
|
A743 CA40 |
1.4028-1.4729 |
J91153 |
|
ACEROS RESISTENTES AL DESGASTE (NI HARD) |
A351 CF3 |
1.4306-1.4309 |
J92500 |
|
DESCRIPCION |
EQUIVALENTES |
COMPOSICION QUIMICA |
PROPIEDADES |
A351 CF3A |
1.4306-1.4309 |
J92500 |
|
|
%C %Si %Mn %S %P %Ni % Cr %Mo |
|
A743 CA6NM |
1.4313-1.4317 |
|
|
NI- HARD 1 |
|
3-3,6 0,3-0,5 0,3-0,7 Max 0,15 Max 0,3 3,3-4,8 1,5-2,6 max 0,4 |
53-61 RC |
AISI 316 |
1.4401-1.4436 |
S31600 |
|
NI- HARD 2 |
|
<2,9 0,3-0,5 0,3-0,7 Max 0,15 Max 0,3 3,3-5 1,4-2,4 max 0,4 |
52-59 RC |
AISI 316 L |
1.4404-1.4432 |
S31603 |
|
NI- HARD 3 |
|
1-1,6 0,4-0,7 0,4-0,7 Max 0,05 Max 0,05 4-4,75 1,4-1,8 |
|
A351 CF3M |
1.4404-1.4435 |
J92800 |
|
NI- HARD 4 |
|
2,6-3,2 1,8-2 0,4-0,6 Max 0,1 Max 0,06 5-6,5 8-9 max 0,4 |
|
A890 Gr5A |
1.4469-1.4517 |
J93404 |
|
|
|
|
|
A 439GrD-2B |
|
F43001 |
|
ACEROS AL MANGANESO
|
A216 WCA |
|
J02502 |
|
DESCRIPCION |
EQUIVALENTES |
COMPOSICION QUIMICA |
PROPIEDADES |
A216 WCC |
|
J02503 |
|
|
%C %Mn %Ni % Cr %Mo % V % Si |
|
A351 CH20 |
|
J93402 |
|
GX120Mn12 |
ASTM A128 Grade A |
1,20 12,00 |
|
A352 LCA |
|
J02504 |
|
GX100Mn12 |
ASTM A128 Grade B1 |
1,00 12,00 |
|
A352 LCC |
|
J02505 |
|
GX120MnCr12.2 |
ASTM A128 Grade C |
1,30 13,00 2,00 |
|
A436 ( Ni Resist) |
|
|
|
GX120MnMo12.1 |
ASTM A128 Grade E1 |
1,20 12,00 1,00 |
|
A532 ( Ni Hard ) |
|
J02505 |
|
GX120MnCrMo 7.1.1 |
|
1,20 8,00 1,00 1,00 |
R>70kg/mm2 |
A781CD4MCu |
|
J93370 |
|
GX150MnCr 18-3 |
|
1,50 19,00 3,00 |
R>70kg/mm2 |
A890 Gr1A |
|
J93370 |
|
|
|
|
|
A890 Gr1B |
|
J93345 |
|
ACEROS REFRACTARIOS
|
A890 Gr2A |
|
J93345 |
|
DESCRIPCION |
EQUIVALENTES |
COMPOSICION QUIMICA |
PROPIEDADES |
A890 Gr6A |
|
J93380 |
|
|
%C %Mn %Ni % Cr %Nb |
|
AM-45 |
|
|
|
GX40CrNiSi 25.12 |
ASTM A297 HH |
0,3-0,5 0,5-1,5 11-14 24-26 |
1100 ºC |
AM45b |
|
|
|
GX40CrNiSi 25.20 |
ASTM A297 HK |
0,3-0,5 0,5-1,5 19-21 24-26 |
1150 ºC |
AM-45c |
|
|
|
GX35CrNiSi 17.37 |
ASTM A297 HU |
0,2-0,5 0,3-1,5 36-39 16-19 |
1120 ºC |
GS-25CrMo4 |
|
|
|
GX45CrSi 29 |
ASTM A297 HC |
0,3-0,6 0,5-1,0 27-30 |
1150 ºC |
GS-45 |
|
|
|
|
ASTM A560 50/50 |
<0,10 <0,30 resto 48-52 |
1150 ºC |
GS-52 |
|
|
|
|
ASTM A560 50Cr50Ni Nb |
<0,10 <0,30 resto 47-52 1,4-1,17 |
1000 ºC |
GS-60 |
|
|
|
|
ASTM A560 60/40 |
<0,10 <0,30 resto 58-62 |
|
GX40 CrNiSi27-4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ACEROS MARTENSITICOS
|
|
|
|
|
DESCRIPCION |
COMPOSICION QUIMICA |
PROPIEDADES |
|
|
|
|
|
%C %Si %Mn %S %P %Ni % Cr %Mo |
|
|
|
|
|
GX50Cr5Mo 0,4 |
0,45-0,55 0,9-1 0,6-1 <0,02 < 0,03 0,3-0,4 4,5-5,5 0,8-0,9 |
470-500 HB |
|
|
|
|
GX45Cr3Mo 0,4 |
0,42-0,52 0,3-0,6 0,6-1 <0,02 < 0,03 11,5-14 0,4 |
|
|
|
|
|
GX50Cr5Mo 0,4Ni0,2 |
0,45-0,55 0,3-0,6 0,6-1 <0,02 < 0,03 0,1-0,2 4,5-5,5 0,3-0,5 |
|
|
|
|
|
GX20Cr10 |
0,18-0,22 0,4-0,5 0,7-1 <0,02 < 0,03 4,1-5,6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ACEROS INOXIDABLES MARTENSITICOS
|
|
|
|
|
DESCRIPCION |
COMPOSICION QUIMICA |
PROPIEDADES |
|
|
|
|
|
%C %Si %Mn %S %P %Ni % Cr %Mo |
|
|
|
|
|
GX4CrNi13-4 QT1 |
<0,06 <1,00 <1,00 <0,03 <0,04 3,5-4,5 11,5-14 0,4-1 |
760MPa |
|
|
|
|
GX4CrNi13-4 QT2 |
<0,06 <1,00 <1,00 <0,03 <0,04 3,5-4,5 11,5-14 0,4-1 |
900MPa |
|
|
|
|
GX4CrNi13-4 QT3 |
<0,03 <1,00 <1,00 <0,025 <0,035 3,5-5 12-13,5 <0,7 |
700MPa |
|
|
|
|
GX4CrNiMo16-5-1+ QT |
<0,06 <0,80 <1,00 <0,025 <0,035 4-6 15-17 0,7-1,5 |
760MPa |
|
|
|
|
ASTM A743 Gr CA6NM |
<0,06 <1,00 <1,00 <0,03 <0,04 3,5-4,5 11,5-14 0,4-1 |
285HB |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ACEROS INOXIDABLES
|
|
|
|
|
DESCRIPCION |
EQUIVALENTES |
COMPOSICION QUIMICA |
PROPIEDADES |
|
|
|
|
|
%C %Mn %Ni % Cr %Mo |
|
|
|
|
|
GX5CrNi |
ASTM A351 CF8 |
<0,08 <1,5 8- 18- 0,5 |
R>45kg/mm2 A>35 |
|
|
|
|
GX12Cr |
ASTM A351 CA (CA15/CA40) |
<0,15 <1,0 <1,0 11,5- |
R>63kg/mm2 A>18 |
|
|
|
|
GX5CrMo |
ASTM A351 CF8M |
<0,08 <1,5 9- 18- 2,0- |
R>45kg/mm2 A>30 |
|
|
|
|
GX2CrMo (316L) |
ASTM A351 CF3M |
<0,03 <1,5 12- 17- 2,5- |
R>45kg/mm2 A>30 |
|
|
|
|
DUPLEX 1.4462-1.4470 |
|
<0,03 <2 4,5-6,5 21-23 2,5-3,5 |
C.R 700-900 Mpa |
|
|
|
|
SUPERDUPLEX A890 |
|
<0,03 <1,5 6-8 24-26 4,0-5 |
C.R>690Mpa |